很遺憾,因您的瀏覽器版本過低導致無法獲得最佳瀏覽體驗,推薦下載安裝谷歌瀏覽器!

<strike id="z1ldl"></strike>
<strike id="z1ldl"></strike>
<strike id="z1ldl"></strike>
<strike id="z1ldl"><dl id="z1ldl"><ruby id="z1ldl"></ruby></dl></strike><strike id="z1ldl"><dl id="z1ldl"><del id="z1ldl"></del></dl></strike>
<span id="z1ldl"><dl id="z1ldl"></dl></span>
<strike id="z1ldl"><i id="z1ldl"></i></strike>
<progress id="z1ldl"><video id="z1ldl"></video></progress>
<span id="z1ldl"><video id="z1ldl"><ruby id="z1ldl"></ruby></video></span>
<strike id="z1ldl"><dl id="z1ldl"></dl></strike>
<strike id="z1ldl"></strike>
<strike id="z1ldl"><dl id="z1ldl"></dl></strike>
<strike id="z1ldl"><i id="z1ldl"></i></strike><span id="z1ldl"></span>
<strike id="z1ldl"></strike>
<strike id="z1ldl"><dl id="z1ldl"><cite id="z1ldl"></cite></dl></strike>

你知道原材料對西安鍛件質量的影響嗎?

2019-10-29  來自: http://www.yaofuli.net/Product-detail-id-1246029.html 瀏覽次數:496

    原材料的良好質量是保證鍛件質量的先決條件,如原材料存在缺陷,將影響西安鍛件的成形過程及西安鍛件的最終質量。如原材料的化學元素超出規定的范圍或雜質元素含量過高,對鍛件的成形和質量都會帶來較大的影響,例如:S、B、Cu、Sn等元素易形成低熔點相,使鍛件易出現熱脆。為了獲得本質細晶粒鋼,鋼中殘余鋁含量需控制在范圍內,例如Al酸0.02%~0.04%(質量分數)。含量過少,起不到控制晶粒長大的作用,常易使鍛件的本質晶粒度不合格;含鋁量過多,壓力加工時在形成纖維組織的條件下易形成木紋狀斷口、撕痕狀斷口等。又如,在1Cr18Ni9Ti

西安鍛造

    奧氏體不銹鋼中,Ti、Si、Al、Mo的含量越多,則鐵素體相越多,鍛造時愈易形成帶狀裂紋,并使零件帶有磁性。


    如原材料內存在縮管殘余、皮下起泡、嚴重碳化物偏析、粗大的非金屬夾雜物(夾渣)等缺陷,鍛造時易使陜西鍛件產生裂紋。原材料內的樹枝狀晶、嚴重疏松、非金屬夾雜物、白點、氧化膜、偏析帶及異金屬混人等缺陷,易引起鍛件性能下降。原材料的表面裂紋、折疊、結疤、粗晶環等易造成鍛件的表面裂紋。